3M EC-1357
Harmonization Code : 3506.91.90.99 | Prepared glues and other prepared adhesives, not elsewhere specified or included; products suitable for use as glues or adhesives, put up for retail sale as glues or adhesives, not exceeding a net weight of 1 kg ; Adhesives based on polymers of headings 3901 to 3913 or on rubber; Other ; Other
Main features
- Fast Interior Contact Assembly
- Positioning Time Before Contact
- Flexible Coating Method Selection
Product Description
3M Scotch-Weld Neoprene High Performance Contact Adhesive EC-1357 is a fast-acting neoprene contact adhesive for aircraft-interior assemblies using rubber, fabric, foam, metal, wood veneer, plastic laminate, or honeycomb. Apply it by spray, brush, or roller, then use the 10 to 20 minute open time to align parts before contact. Qualified canvas-to-steel peel strength reaches 42 lb/in width after five days at 24 deg C, while three-week birch overlap shear reaches 536 psi at 24 deg C and 199 psi at 82 deg C.
Key features
- Rapid Contact Strength Build: The adhesive develops high initial strength for efficient assembly.
- Positioning Time Before Contact: A 10 to 20 minute open time supports alignment and adjustment.
- Spray Brush Or Roller Application: Multiple coating methods accommodate varied part sizes and shapes.
Applications
Aircraft-interior panels, wood veneer, rubber, fabric, foam, metal, plastic laminate, and compatible honeycomb assembly.
Technical Specifications
No specifications available.
Additional Information
After-processing / final-state properties
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| 180 deg peel strength | 42 | lb/in width | Canvas to steel after 5 days at 24 deg C |
| Overlap shear strength | 536 | psi | Birch to birch after 3 weeks at 24 deg C |
| Low-temperature overlap shear strength | 964 | psi | Birch to birch after 3 weeks; tested at -34 deg C |
| High-temperature overlap shear strength | 199 | psi | Birch to birch after 3 weeks; tested at 82 deg C |